Comparison between different fracture toughness techniques in zirconia dental ceramics.

Vickers indentation (IF) and single-edge-V-notched beam (SEVNB), to measure the fracture toughness (KIC ) of zirconia-based dental ceramics and mathematical models were proposed to establish a correlation between both. Zirconia (ZrO2 ) stabilized with 3 mol. % of Y2 O3 (3Y-TZP) and 5 mol% of Y2 O3 (5Y-PSZ) were compacted (n = 42) and sintered for 2 h at different temperatures (1475°C, 1500°C, 1550°C, or 1600°C). After sintering, they were characterized by relative density using the ASTM C373-88 standard, X-ray diffraction (XRD) and scanning electron microscopy (SEM). The average grain size was measured according to the ASTM E1382-97 standard. The fracture toughness (KIC ) was determined using two methods: Vickers indentation fracture toughness (KIC-IF ): method based on mathematical modeling that considers the parameters used for the Vickers hardness test and Fracture toughness by the single-edge-V-notch-beam (KIC-SEVNB ): method proposed by ISO 23146:08. The main phases of the 3Y-TZP and 5Y-PSZ ceramics were ZrO2 -tetragonal and ZrO2 -cubic, respectively. The 3Y-TZP specimens showed equiaxed grains with average grain sizes ranging from 0.55 to 0.79 µm. The grain sizes of 5Y-PSZ of specimens sintered at 1475°C and 1600°C were 0.62 and 2.32 µm, respectively. For all ceramics the crack size ratio was c/a < 2.5, suggesting a Palmqvist-type crack system. The fracture toughness measured by the Vickers indentation method (KIC-IF ) and by the SEVNB method (KIC-SEVNB ) was the same when the experimental data were fit to a mathematical model.

Comparison of the indentation strength and single-edge-v-notched beam methods for dental ceramic fracture toughness testing

Aim: To study influence of the cooling rate after sintering a veneering porcelain (Vita VM9) on fracture toughness by indentation strength (IS) and single-edge-v-notched beam (SEVNB) methods. Methods: Vita VM9 bars were sintered according to the manufacturer's recommendation and cooled under three conditions: Slow (inside the furnace from sintering temperature to room temperature); Normal (inside the furnace from sintering temperature to 500 ºC and outside the furnace from 500 ºC to room temperature); and Fast (outside the furnace from sintering temperature to room temperature). Fracture toughness was measured by IS (n=10) and SEVNB (n=10) methods. Data were analyzed by two-way ANOVA (α=0.05). Results: The fracture toughness obtained from SEVNB (slow - 1.02±0.10; normal - 1.09±0.13; and fast - 1,02±0.18 MPa.m1/2 cooling techniques) was significantly lower than IS (slow - 1.19±0.13; normal - 1.17±0.07; and fast - 1.16±0.06 MPa. m1/2 cooling techniques). There was no significant influence of the cooling technique (p=0.012). Conclusions: The measurement technique influenced the fracture toughness values . IS method overestimated the fracture toughness values. Irrespective of the measuring method, cooling rate did not influence the Vita VM9 veneering porcelain fracture toughness (Au)

FEA and microstructure characterization of a one-piece Y-TZP abutment.

OBJECTIVES: The most important drawback of dental implant/abutment assemblies is the need for a fixing screw. This study aimed to develop an esthetic one-piece Y-TZP abutment to suppress the use of the screw. METHODS: Material characterization was performed using a bar-shaped specimen obtained by slip-casting to validate the method prior to prototype abutment fabrication by the same process. The mechanical behavior of the prototype abutment was verified and compared with a conventional abutment by finite element analysis (FEA). The abutment was evaluated by micro-CT analysis and its density was measured. RESULTS: FEA showed stress concentration at the first thread pitch during installation and in the cervical region during oblique loading for both abutments. However, stress concentration was observed at the base of the screw head and stem in the conventional abutment. The relative density for the fabricated abutment was 95.68%. Micro-CT analysis revealed the presence of elongated cracks with sharp edges over the surface and porosity in the central region. SIGNIFICANCE: In the light of these findings, the behavior of a one-piece abutment is expected to be better than that of the conventional model. New studies should be conducted to clarify the performance and longevity of this one-piece Y-TZP abutment.

Controle do tombamento de plântulas de algodoeiro, causado por Rhizoctonia solani, através do tratamento de sementes / Control damping off on cotton seedlings caused by Rhizoctonia solani through seed treatment

O tombamento de plântulas, causado por Rhizoctonia solani, é considerado uma das mais importantes doenças do algodoeiro. Esse patógeno habitante do solo, sobrevive na matéria orgânica ou restos vegetais e pode ser transmitido para as sementes. O objetivo deste trabalho foi avaliar o efeito do tratamento de sementes com fungicidas no controle do tombamento de plantas causado por R. solani. Os tratamentos utilizados foram: 1) testemunha não inoculada; 2) testemunha inoculada; 3) fluazinam + tiofanato metílico (115,5 + 17,33 g 100 kg-1 sementes); 4) fluazinam + tiofanato metílico (150,5 + 22,58 g 100 kg-1 sem.); 5) fluazinam + tiofanato metílico (185,5 + 27,83 g 100 kg-1 sem.); 6) pencicurom (75 g 100 kg-1 sem.); 7) tolifluanida (100 g 100 kg-1 sem.): 8) carbendazim + tiram (90 + 120 g 100 kg-1 sem.) e 9) fludioxonil (5 g 100 kg-1 sem.). Foi avaliada a emergência de plântulas aos 07 e 26 DAS, a porcentagem de incidência de sintomas, a severidade, a altura de plântulas, o comprimento de raiz e a massa de matéria seca aos 26 DAS. O fungicida fluazinam + tiofanato metílico nas doses de 115,5 + 17,33 g i.a. 100-1 kg de sementes, 150,5 + 22,58 g i.a. 100-1 kg de sementes e o fungicida tolifluanida na dose de 100 g i.a. 100-1 kg de sementes, mostram-se eficientes no controle de tombamento do algodoeiro causado por Rhizoctonia solani, podendo a mistura de fluazinam + tiofanato metílico ser recomendada para o controle deste patógeno. Plântulas do tratamento testemunha inoculada apresentaram menor altura, caracterizando menor desenvolvimento inicial da cultura, sendo então adequado o tratamento de sementes com fungicidas.

Damping off, caused by Rhizoctonia solani, is one of the most important cotton diseases. This soil pathogen, survives in organic matter and can be transmitted by seeds. The objective of this study was evaluate the effect of seeds treatment with a fungicides for control of damping off, caused by R. solani. The evaluated treatments were as follows: 1) untreated check without inoculation; 2) untreated check with inoculation; 3) fluazinam + thiophanate-methyl (115,5 + 17,33 g.100 kg-1 seeds); 4) fluazinam + thiophanate-methyl (150,5 + 22,58 g.100 kg-1 seeds); 5) fluazinam + thiophanate-methyl (185,5 + 27,83 g.100 kg-1 seeds); 6) pencycuron (75 g.100 kg-1 seeds); 7) tolylflouanid (100 g.100 kg-1 seeds): 8) carbendazin + thiram (90 + 120 g.100 kg-1 seeds) and 9) fludioxonil (5 g.100 kg-1 seeds). It was evaluated the plant population at 7 and 26 days after sowing; incidence and severity of the disease; seedling height; root length and dry weight at 26 days afeter sowing. The fungicide fluazinam + thiophanate methyl doses 115,5 + 17,33 g i.a. 100-1 kg seeds, 150,5 + 22,58 g i.a. 100-1 kg seeds and the fungicide tolylfluanid doses 100 g i.a. 100-1 kg seeds, showed control efficiency of cotton dumping off caused by Rhizoctonia solani, can be recommended to this pathogen control. Seedlings of untreated check with inoculation showed short height, characterizing less start development of the culture, been recommended the seed treatment with fungicides.

Amálgama dental: estudo da microdureza superficial: efeito da brunidura / Dental amalgan: a study of the superficial micro-hardness: the effect of overheating on amalgam hardness

Os autores estudaram a microdureza superficial de amálgamas feitos com liga convencional e com liga de maior conteúdo de cobre com objetivo de verificar os efeitos produzidos pela brunidura, nas idades de 24 e 168 horas. Os resultados obtidos permitem afirmar que a microdureza de todos os amálgamas estudadas aumentou com o tempo. Os valores médios encontrados para as margens e para o centro säo estatisticamente semelhantes. Os amálgamas feitos com ligas de maior conteúdo de cobre apresentaram valores de microdureza mais elevados do que as ligas convencionais

Resistência à fratura de dentes com cúspides socavadas e restaurados com diferentes materiais / Fracture resistence of teeth with undermined cusps and with cusps restored with different materiais

O preparo cavitário geralmente diminui a resistência à fratura dos dentes, principalmente quando a largura da caixa oclusal da cavidade é de um terço ou mais da distância intercuspídea. Dependendo do material restaurador empregado, esses dentes apresentam grande variaçäo na resistência à fratura. Neste trabalho, foi comparada a resistência à fratura de dentes pré-molares superiores com preparo cavitário mésio-oclusal com a cúspide vestibular socavada com a resistência à fratura de dentes com esse mesmo tipo de cavidade e restaurados com resina composta com adesivo dental, a amálgama com base de resina composta e amálgama com base de cimento ionômero de vidro. Os dentes testados foram submetidos à carga de compressäo numa máquina de ensaios Universal Kratos com velocidade controlada. Os dentes restaurados com resina composta e com amálgama mais base de resina composta apresentaram resistência à fratura semelhante entre si e estatisticamente mais elevada que a resistência à fratura dos dentes apenas preparados. Os restaurados com amálgama e com base de cimento ionômero de vidro apresentaram resistência à fratura estatisticamente semelhante à dos dentes apenas preparados

Amálgama dental: estudo da emissao de vapor de mercúrio, efeito de tempo, brunidura e verniz / Dental amalgam: study of mercury emission, effect of time, burnishing and varnish

Os autores estudaram a emissao de vapor de mercúrio de amálgamas, convencional e com maior conteúdo de cobre com o objetivo de verificar os efeitos produzidos pela brunidura, pela aplicaçao de verniz e tempo. As dosagens de mercúrio foram realizadas, após a condensaçao do amálgama, com um espectrofotômetro de absorçao atômica, com câmara de captaçaode vapor de mercúrio. Nas condiçoes experimentais estudadas podemos afirmar que a emissao é mais intensa nos primeiros tempos com características de decrescer em funçao do tempo e se estabiliza a partir de 60 minutos. Os resultados obtidos mostram que a liga com maior conteúdo de cobre emite maior quantidade de vapor de mercúrio nos períodos iniciais quando comparada com os amálgamas obtidos das ligas convencionsis que tem médias semelhantes entre si. Os amálgamas apenas esculpidos emitem maior quantidade de mercúrio quando comparadas aqueles que foram brunidos com ou sem aplicaçao de verniz cavitário, ou com aqueles que foram apenas esculpidos, tendo sido condensados após a aplicaçao de verniz cavitário

Absorção de líquido das resinas compostas: 131.490 horas de teste de sorpção de líquido aquoso / Composite resins absorption of liquids: 131.490 hours test of sorption in H2O liquid

Neste trabalho, foi analisada a embebição de águas das resinas, acrílicas e compostas, nos períodos de 24h e 131.466h. totalizando 131.490 horas de teste à temperatura de 37ºC e ambiente

Microdureza das margens de restauraçöes com amálgama / Margin microhardness of dental amalgam fillings

Realizaram-se restauraçöes com amálgama preparadas com quatro diferentes limalhas, em corpos-de-prova confeccionados com dentes naturais recentemente extraídos. Decorridas 24 horas, os excessos eram removidos com três diferentes instrumentos rotatórios em ultra-alta velocidade, e em seguida o polimento era completado. Após esse polimento, passava-se ao polimento metalográfico, e em seguida realizavam-se as medidas de microdureza Vickers, em uma das margens da restauraçäo. Cento e sessenta e oito horas após a condensaçäo, realizavam-se outras medidas. Os resultados obtidos permitem afirmar que um dos instrumentos, a broca multilaminada, induziu um aumento da microdureza, enquanto os outros dois (broca Roto Pro 404 e ponta de carboneto de silício) mostraram valores estatisticamente semelhantes aos do grupo controle